LNP Thermocomp? LF-1006 Polyetheretherketone, Glass Fiber Reinforcement 物性表: LNP Thermocomp? LF-1006 Polyetheretherketone, Glass Fiber Reinforcement物性表及特性介紹,LNP Thermocomp? LF-1006 Polyetheretherketone, Glass Fiber Reinforcement注塑參數詳情,如需LNP Thermocomp? LF-1006 Polyetheretherketone, Glass Fiber Reinforcement下載, 可到相關下載區下載
  • 吸水率 [%]: 0.1
  • 缺口沖擊強度: 1.17
  • 拉伸強度 [MPa]: 176.0
  • 彎曲模量 [MPa]: 10.8
  • 熱變形溫度 [℃]: 299.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.53 g/cc1.53 g/ccMethod A; ASTM D792
Water Absorption 0.10 %0.10 %at 24 hrs; ASTM D570
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 176 MPa25500 psiASTM D638
Tensile Strength, Yield 176 MPa25500 psiASTM D638
Elongation at Break 2.0 %2.0 %ASTM D638
Elongation at Yield 2.0 %2.0 %ASTM D638
Tensile Modulus 13.2 GPa1910 ksiASTM D638
Flexural Strength 241 MPa35000 psiASTM D790
Flexural Modulus 10.8 GPa1570 ksiASTM D790
Izod Impact, Notched 1.17 J/cm
@Thickness 3.18 mm
2.19 ft-lb/in
@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 8.75 J/cm
@Thickness 3.18 mm
16.4 ft-lb/in
@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 11.6 kJ/m25.52 ft-lb/in2ISO 180
Izod Impact, Unnotched (ISO) 57.3 kJ/m227.3 ft-lb/in2ISO 180
Falling Dart Impact 13.7 J10.1 ft-lbASTM D3763
 
Thermal PropertiesMetricEnglishComments
CTE, linear 17.0 μm/m-°C
@Temperature 20.0 °C
9.44 μin/in-°F
@Temperature 68.0 °F
ISO 11359-1, -2
CTE, linear, Transverse to Flow 48.0 μm/m-°C
@Temperature 20.0 °C
26.7 μin/in-°F
@Temperature 68.0 °F
ISO 11359-1, -2
Deflection Temperature at 0.46 MPa (66 psi) 299 °C570 °FUnannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 299 °C570 °FUnannealed; ASTM D648
Flammability, UL94 V-0
@Thickness 0.780 mm
V-0
@Thickness 0.0307 in
 
Processing PropertiesMetricEnglishComments
Melt Temperature 379 - 388 °C714 - 730 °F
Mold Temperature 135 - 163 °C275 - 325 °F
Drying Temperature 121 - 149 °C250 - 300 °F
Dry Time 4 hour4 hour
Moisture Content 0.10 %0.10 %Suggested
Back Pressure 0.345 - 0.689 MPa50.0 - 99.9 psi

轉載請注明: 轉自中國塑膠原料之家 http://www.sgwanshunchem.com/wuxingbiao/

本文鏈接: http://www.sgwanshunchem.com/yuanliaoku/show-50418.html

免責聲明: 本文 LNP Thermocomp? LF-1006 Polyetheretherketone, Glass Fiber Reinforcement 僅代表作者個人觀點,中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容,其版權均由原作者和資料提供方所擁有!如因作品版權問題需要處理,請與我們聯絡

塑膠原料之家,專業塑料網站、原料報價網站,免費發布塑膠供求信息。塑膠原料之家為您提供塑料供應、塑料求購、塑料行情、塑料展會、塑料原料資訊服務。

2008-2015 塑料|塑膠原料|物性表大全|UL黃卡|SGS報告查詢|最新價格--塑膠原料之家

滬ICP備15027283號-4

她的小梨涡txt百度网盘下载