Wolf Kunststoff ZEDEX? ZX-324V11T A3L PEEK Polymer, Reinforced

Wolf Kunststoff ZEDEX? ZX-324V11T A3L PEEK Polymer, Reinforced 物性表: Wolf Kunststoff ZEDEX? ZX-324V11T A3L PEEK Polymer, Reinforced物性表及特性介紹,Wolf Kunststoff ZEDEX? ZX-324V11T A3L PEEK Polymer, Reinforced注塑參數詳情,如需Wolf Kunststoff ZEDEX? ZX-324V11T A3L PEEK Polymer, Reinforced下載, 可到相關下載區下載
  • 密度 [g/cm3]: 1.34
  • 吸水率 [%]: 0.05
  • 拉伸強度 [MPa]: 78.0
  • 彎曲模量 [MPa]: 2.937
 
Physical PropertiesMetricEnglishComments
Density 1.34 g/cc0.0484 lb/in3ISO 1183
Water Absorption 0.050 %
@Temperature 23.0 °C
0.050 %
@Temperature 73.4 °F
RMC 93%; DIN EN ISO 62
Moisture Absorption at Equilibrium 0.10 %0.10 %DIN EN ISO 62
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore A >= 100>= 100DIN 53505
Hardness, Shore D 8585DIN 53505
Ball Indentation Hardness 190 MPa27600 psiDIN 2039
Tensile Strength at Break 98.0 MPa14200 psiDIN EN ISO 527
Tensile Strength 113 MPa16400 psiDIN EN ISO 527
Tensile Stress 29.0 MPa
@Strain 1.00 %,
Time 3.60e+6 sec
4210 psi
@Strain 1.00 %,
Time 1000 hour
DIN 53444
Tensile Strength, Yield 78.0 MPa11300 psiElastic Limit
 113 MPa16400 psiDIN EN ISO 527
Elongation at Break 9.0 %9.0 %
 9.0 %9.0 %DIN EN ISO 527
Elongation at Yield 1.3 %1.3 %Elastic Yield Point
 5.0 %5.0 %Elongation at Maximum Force; DIN EN ISO 527
 5.0 %5.0 %Yield Strain; DIN EN ISO 527
 6.6 %6.6 %Flexural; DIN EN ISO 178
Tensile Modulus 4.40 GPa638 ksiDIN EN ISO 527
Flexural Strength 119 MPa17300 psiOuter Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178
 159 MPa23100 psiDIN EN ISO 178
Flexural Modulus 2.937 GPa426.0 ksiDIN EN ISO 178
Compressive Yield Strength 146 MPa21200 psiDIN EN ISO 604
Compressive Strength 122 MPa17700 psiElastic Limit
 40.0 MPa
@Time 3.60e+7 sec
5800 psi
@Time 10000 hour
 103 MPa
@Time 360000 sec
14900 psi
@Time 100 hour
 130 MPa
@Time 36.0 sec
18900 psi
@Time 0.0100 hour
 36.0 MPa
@Strain 3.50 %
5220 psi
@Strain 3.50 %
DIN EN ISO 604
Compressive Modulus 2.85 GPa413 ksiDIN EN ISO 604
Fatigue Strength 65.0 MPa
@Frequency 1.00 Hz,
Temperature 20.0 °C
9430 psi
@Frequency 1.00 Hz,
Temperature 68.0 °F
10° stress cycles
K Factor (ISO)  1.2 μm/km
@Temperature 200 °C
1.2 μm/km
@Temperature 392 °F
 3.7 μm/km
@Temperature 240 °C
3.7 μm/km
@Temperature 464 °F
 9.1 μm/km
@Temperature 100 °C
9.1 μm/km
@Temperature 212 °F
 12 μm/km
@Temperature 20.0 °C
12 μm/km
@Temperature 68.0 °F
Charpy Impact Unnotched NBNBEN ISO 179/1eU
Charpy Impact, Notched 0.620 J/cm22.95 ft-lb/in2EN ISO 179/1eA
Coefficient of Friction, Dynamic  0.14
@Temperature 20.0 °C
0.14
@Temperature 68.0 °F
Dry Operation
 0.21
@Temperature 100 °C
0.21
@Temperature 212 °F
Dry Operation
Coefficient of Friction, Static 0.18
@Temperature 20.0 °C
0.18
@Temperature 68.0 °F
Dry Operation
Tensile Creep Modulus, 1000 hours 2780 MPa403000 psiAt 1% Deformation; DIN 53444
Limiting Pressure Velocity 0.300 MPa-m/sec8570 psi-ft/minv = 200m/min
 0.33333 MPa-m/sec9516.6 psi-ft/minv = 100m/min
 0.91666 MPa-m/sec26171 psi-ft/minv = 10m/min
 1.00 MPa-m/sec28600 psi-ft/minv = 1m/min
Compression Set 8.3 %8.3 %Elastic Compression Limit
 12.5 %12.5 %Nominal Compressive Yield Strain; DIN EN ISO 604
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 4.00e+15 ohm-cm4.00e+15 ohm-cmIEC 93
Surface Resistance 7.80e+11 ohm7.80e+11 ohmIEC 93
Dielectric Constant 3.0
@Frequency 110 Hz
3.0
@Frequency 110 Hz
IEC 250
Dielectric Strength 26.0 kV/mm660 kV/inIEC 243
Dissipation Factor 0.00200.0020IEC 112
 0.053
@Frequency 1.00 Hz
0.053
@Frequency 1.00 Hz
 
Thermal PropertiesMetricEnglishComments
CTE, linear  58.0 μm/m-°C
@Temperature <=100 °C
32.2 μin/in-°F
@Temperature <=212 °F
ISO E 830
 58.0 μm/m-°C
@Temperature <=150 °C
32.2 μin/in-°F
@Temperature <=302 °F
ISO E 831
Specific Heat Capacity 0.900 J/g-°C0.215 BTU/lb-°FDSC
Thermal Conductivity 0.240 W/m-K1.67 BTU-in/hr-ft2-°FDIN 52612
Melting Point 340 °C644 °FDSC
Maximum Service Temperature, Air 140 °C284 °FPressed Bushings
 250 °C482 °FContinuous
 260 °C500 °FShort Term (3h)
Deflection Temperature at 1.8 MPa (264 psi) 165 °C329 °FDIN EN ISO 75
Glass Transition Temp, Tg 146 °C295 °FDSC
Flammability, UL94 V-0V-0
 
Descriptive Properties
Alignment Adjustment4Nominal Scale: 1, low; 10, high
Chemical Sterilization10Nominal Scale: 1, low; 10, high
ColorBlack
Creep Resistance5Nominal Scale: 1, low; 10, high
Dimensional Stability with Thermal Expansion5Nominal Scale: 1, low; 10, high
Free from SiliconApplicable
Gamma-rays Radiation Sterilization10Nominal Scale: 1, low; 10, high
High Precision Bushings (negative clearance)Applicable
Injection Molded PartsApplicable
Machined PartsApplicable
Moist Heat Sterilization10Nominal Scale: 1, low; 10, high
Plastic GranulesApplicable
Resistance Against dust, Dirt, Abrasive Substances7Nominal Scale: 1, low; 10, high
Resistance Against Hot Water200
Resistance to Chemicals8Nominal Scale: 1, low; 10, high
Resistant Against DisinfectantApplicable
Rods up to ?e (de)Applicable
ROHS/WEEEApplicable
Sheets up to Maximum ThicknessApplicable
Sliding Velocity100
Suitable for Outdoor Use7Nominal Scale: 1, low; 10, high
Suitable for Use in WaterApplicable
Suitable for VacuumApplicable
Tubes (hollow rods) up to ?e (de)Applicable
UV Rays Resistance9Nominal Scale: 1, low; 10, high
UV-Sterilization7Nominal Scale: 1, low; 10, high

轉載請注明: 轉自中國塑膠原料之家 http://www.sgwanshunchem.com/wuxingbiao/

本文鏈接: http://www.sgwanshunchem.com/yuanliaoku/show-50414.html

免責聲明: 本文 Wolf Kunststoff ZEDEX? ZX-324V11T A3L PEEK Polymer, Reinforced 僅代表作者個人觀點,中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容,其版權均由原作者和資料提供方所擁有!如因作品版權問題需要處理,請與我們聯絡

塑膠原料之家,專業塑料網站、原料報價網站,免費發布塑膠供求信息。塑膠原料之家為您提供塑料供應、塑料求購、塑料行情、塑料展會、塑料原料資訊服務。

2008-2015 塑料|塑膠原料|物性表大全|UL黃卡|SGS報告查詢|最新價格--塑膠原料之家

滬ICP備15027283號-4

她的小梨涡txt百度网盘下载